|Place of Origin:||Anhui|
|Minimum Order Quantity:||1000kgs|
|Price:||USD1.8/kg to USD2.0/kg FOB Qingdao Port,China|
|Packaging Details:||1kg/PE film bag, 20kg/Plastic Woven bag,9000kgs/20'gp|
|Delivery Time:||Within 15days after order confirmation|
|Payment Terms:||L/C, D/A, D/P, T/T, Western Union, MoneyGram|
|Supply Ability:||10000TON PER YEARS|
|Material:||PP Resin||Length:||Times Of 4mm/5mm/6mm|
|Crack Elongation::||20+/-5%||Fiber Diameter:||20-30um|
|Melting Point(C Deg.):||160 - 170||Density(g/cm3):||0.91+/-0.01|
|Tensile Strength(MPa):||450 Min.||Acid &Alkali Resistance:||Strong|
Microfiber Monofilament PP Polypropylene Fiber For Concrete
EltFiber-PPMF monofilament fiber was produced by referring foreign advanced technology for fiber spinning, modified by adding functional additive and special surface-treating. Mixing into cement concrete, it has many advantages such as good dispersing, better water affinity, strong linking force. It is suited to reinforce and crack-resist to every kinds of cement concrete and mortar, specially used in engineering of building surface, floor, wall etc…..
◆Resist to shrink & crack
◆Increase seepage resistance
◆Increase friction resistance
◆Increase freezing & thawing resistance
◆Improve tendons protection
◆Replace steel net (using in plastering)
◆ Prevent mortar split and crackle expansion
◆Increase impact resistance and peeling resistance
• Cost effective
• Replaces anti crack mesh reinforcement
• Decreases construction time and labor
• Inhibits intrinsic cracking in concrete
• Disperses uniformly throughout the mix
• Do not rust
• Explosive spall control
A). suit for the waterproof layer, floor, inner & outer wall of industrial and civil construction.
B). Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in natatorium, swimming pool, pond and ditch.
D). Suit for any mortar projects and common concrete projects.
E). Highway, bridge and other roads.
A). Dosage: for resist the common cracks on surfaces, 0.9kg/m3 fibers to cement mortar
Is enough, and for increasing reinforce and seepage resist application 1.8kg/m3 is enough.
B). Stirring requirement: The proportion of cement, sand and aggregate is no
need to be changed. Put cement, aggregate, additive and fiber together, then stir after
adding enough water and time for stirring can be prolonged for 2~3 minutes in order to
make the compound mix completely. Also it can be mixed with cement and other
aggregates in advance, stirring by adding water at worksite before construction.
ASTM C1116, Type III
BS EN 14889 - 2
1, Normal Type MicroFiber Monofilament PPMF-A
|Raw Material :||Polypropylene||Crack Elongation:||20+/-5%|
|Fiber Type :||Monofilament PPMF-A||Fiber Diameter:||20-30um|
|Melting Point(C Deg.) :||160 - 170||Density(g/cm3) :||0.91+/-0.01|
|Acid &Alkali Resistance :||Strong||Tensile Strength(MPa):||450 min.|
|Length:||Times of 4mm or 6mm||Water absorbency :||NO|
4mm, 6mm, 8mm, 12mm,18mm, 24mm, 30mm etc...
(times of 4mm or 6mm with 1mm more or less )
2,Special Type MicroFiber Monofilament
|PP Fiber Shape||
(PE film bag)
(Plastic Woven bag)
(water Soluble paper bag)