|Place of Origin:||Anhui|
|Minimum Order Quantity:||1000kgs|
|Packaging Details:||120-140g/ water soluble film bundle, 5kgs/water soluble paper carton, total 1200-1300kg/pallet, 12800kg/20'GP, 25800kg/40'GP|
|Delivery Time:||Within 15days after order confirmation|
|Payment Terms:||L/C, D/A, D/P, T/T, Western Union, MoneyGram|
|Supply Ability:||10000TON PER YEARS|
Polypropylene Macro Synthetic Fiber Embossed Form Similar To SIKAfiber Force 48mm 55mm 65mm
Elite Macro Synthetic Fiber of Embossed Form is macro synthetic reinforcing fiber complying with ASTM–C1116 and carries CE Mark,
Type III and EN 14889-2: 2006 Polymer Fibers - Definitions, specifications and conformity.
Elite Macro Synthetic Fiber of Embossed Form is specifically engineered for use as secondary reinforcement.it is a 100% virgin
copolymer fiber designed to provide a high performing reinforcement system for concrete.
Elite Macro Synthetic Fiber of Embossed Form is specifically engineered and manufactured to reduce plastic and hardened concrete
shrinkage,increase fatigue resistance and concrete toughness,and improve impact strength.
|Raw Material||Virgin grade polypropylene/polyethylene blend||Tensile Strength(MPa):||550 min.|
|Water Absorbency:||No||Density(g/cm3) :||0.91+/-0.01|
|Melting Point(C Deg.) :||160 - 170||Acid & Alkali Resistance||Excellent|
|Elastic Modulas(Mpa):||9000 min||Moisture Content||No|
|Length:||48mm, 55mm, 65mm or as per request|
3, Packing & Delivery:
Packing: 120-140g/ water soluble film bundle, 5kgs/water soluble paper carton
total 1200-1300kg/pallet, 12800kg/20’ container, 25800kg/40’ container
|Delivery Time||3-15 days after deposit (we always keep inventory)|
|Sample Time||1-3 days after confirmation|
|Payment Methods||T/T, L/C, Western Union or as per negotiate|
Compared with steel fiber, our fiber has the advantages of anti-corrosion and wear-resistant reducing 50% cost with same volume to steel fiber.
1), Equivalent strengths to WWM and rebar provided by engineering calculations;
2), Controls and mitigates plastic shrinkage cracking and reduces segregation and bleed-water;
3), Provides three-dimensional reinforcement against micro and macro-cracking;
4), Reduces equipment wear, fiber rebound and increases build-up thickness compared to steel fibers for shotcrete applications;
5), Increases overall durability, fatigue resistance and flexural toughness;
6), Reduction of in-place cost versus wire mesh for temperature / shrinkage crack control;
7), Easily added to concrete mixture at any time prior to placement;
8), Tested in accordance with ASTM C 1116, EN14889-2.
■ Industrial and Warehouse Floors
■ Residential and commercial Slab on grade
■ Driveways and side walks
■ Replacement for welded wire fabric (WWF)
■ Composite metal decks and parking structures
■ Septic tanks,manholes and burial vaults
■ Precast elements
■ Shotcrete applications
6, Our Company:
Anhui Elite Industrial Co.,LTD was established in 2007, has become one of the leading and professional suppliers of all kinds of
Concrete Admixture in the world market.
Our Product were widely used in all kinds of concrete,mortar,plaster projects and exported to more than 30 countries, Such as USA,
Russia, Germany, Australia, Chile, UAE, Korea, Vietnam, Africa etc.
Our Fibers was made by 100% Virgin Material with advanced equipment of yard and cutting, we have one full set of precise testing
instrument, testing equipment and quality inspection team, technology research and development team. the management system
was certified by ISO9001 and our products have been passed the CE Certification.
Our Mainly Product and Production Capacity as below:
Polypropylene Fiber (PP Fiber)
Polyester Fiber(PET Fiber)
Polyvinyl Alcohol Fiber( PVA Fiber)
Polyacrylonitrile Fiber(PAN Fiber)
Naphthalene Formaldehyde Sulphonate
7, Related Product:
|Features:||Economy, Durable, High Tensile Strength||Material:||Polypropylene|
|Length:||48mm 55mm 65mm Or As Per Request||Elastic Modulas:||Min 9000MPa|
|Equivalent Diameter:||0.9mm||Melting Point(C Deg.):||160 - 170|
|Density(g/cm3):||0.91+/-0.01||Tensile Strength(MPa):||550 Min.|
|Acid &Alkali Resistance:||Excellent||Application:||Replace Steel Fibers|