Factory Directly Supply Monofilament Microfiber Polypropylene Fiber For Concrete Reinforce
|Minimum Order Quantity :||1000kgs||Price :||Negotiation|
|Packaging Details :||1kg/PE film bag, 20kg/Plastic Woven bag,9000kgs/20'gp||Delivery Time :||Within 15days after order confirmation|
|Payment Terms :||L/C, D/A, D/P, T/T, , MoneyGram||Supply Ability :||10000TON PER YEARS|
|Place of Origin:||Anhui||Brand Name:||ELITE-INDUE|
|Certification:||CE ISO||Model Number:||EltFiber-PPMF|
|Material:||Virgin Homopolymer PP||Length:||6mm 12mm 19mm 24mm|
|Crack Elongation::||20+/-5%||Fiber Diameter:||20-30um|
|Melting Point(C Deg.):||160 - 170||Density(g/cm3):||0.91+/-0.01|
|Tensile Strength(MPa):||450 Min.||Shape:||Multifilament|
|HS CODE:||5503400000||Packing:||PE Film Bag Or Water Soluble Paper Bag|
fibrillated polypropylene fibers,
synthetic polymer fibers
Micro Synthetic Fibre Virgin Homopolymer PP Fiber Multifilament For Concrete
Multifilament Polypropylene Fiber also called Monofilament PP Fiber,
it is easy to finish, fully oriented,100% Virgin Homo-polymer Polypropylene Multi-filament Fibrous Reinforcement.
Our PP Fiber Multifilament was produced by referring foreign advanced technology for fibers pinning, modified by adding functional additive
and special surface-treating.
Mixing into cement concrete, it has many advantages such as good dispersing, better water affinity, strong linking force.
Our Monofilament Polypropylene Fiber offers long term durability, and functions as a plastic shrinkage reinforcement intended
to reduce the formation of shrinkage cracks prior to the initial set.
This Monofilament Fiber is non-corrosive, chemically inert, and 100% Alkali Proof.
A). suit for the waterproof layer, floor, inner & outer wall of industrial and civil construction.
B). Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in natatorium, swimming pool, pond and ditch.
D). Suit for any mortar projects and common concrete projects.
E). Highway, bridge and other roads.
3, Applying Instruction:
A). Dosage: for resist the common cracks on surfaces, 0.9kg/m3 fibers to cement mortar Is enough,
and for increasing reinforce and seepage resist application 1.8kg/m3 is enough.
B). Stirring requirement: The proportion of cement, sand and aggregate is no need to be changed.
Put cement, aggregate, additive and fiber together, then stir after adding enough water and time for stirring can be prolonged for
2~3 minutes in order to make the compound mix completely.
Also it can be mixed with cement and other aggregates in advance,
stirring by adding water at worksite before construction.
4, Brief specification:
ASTM C1116, Type III
BS EN 14889 - 2
1), Normal Type MicroFiber Monofilament PPMF-A
Raw Material :
Fiber Type :
|Monofilament PPMF-A||Fiber Diameter:||20-30um|
Melting Point(C Deg.) :
|160 - 170||Density(g/cm3) :||0.91+/-0.01|
Acid &Alkali Resistance :
|Strong||Tensile Strength(MPa):||450 min.|
|Times of 4mm or 6mm||Water absorbency :||NO|
4mm, 6mm, 8mm, 12mm,18mm, 24mm, 30mm etc...
(times of 4mm or 6mm with 1mm more or less )
2),Special Type MicroFiber Monofilament
A, MicroFiber Monofilament PPMF-B: High Tensile Strength -----------600MPa Min
B, MicroFiber Monofilament PPMF-C: Superfine---------------------------20+/-2um Dia
C, MicroFiber Monofilament PPMF-D: High dispersion------------------Special Surface-Treating
|PP Fiber Shape||
(PE film bag)
(Plastic Woven bag)
(water Soluble paper bag)